Stainless-steel pipe for oil well and process for producing the same

ABSTRACT

A steel composition contains: 0.05% or less of C; 0.5% or less of Si; 0.20% to 1.80% of Mn; 0.03% or less of P; 0.005% or less of S; 14.0% to 18.0% of Cr; 5.0% to 8.0% of Ni; 1.5% to 3.5% of Mo; 0.5% to 3.5% of Cu; 0.05% or less of Al; 0.20% or less of V; 0.01% to 0.15% of N; and 0.006% or less of O on a mass basis, and satisfies the following expressions: Cr+0.65Ni+0.6Mo+0.55Cu−20C≧18.5 and Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11 (where Cr, Ni, Mo, Cu, C, Si, Mn, and N represent their respective contents (mass %)). After such a steel pipe material is formed into a steel pipe, the steel pipe is quenched by cooling after heating to a temperature of the A C3  transformation point or more and tempered at a temperature of the A C1  transformation point or less. The composition may further contain at least one element of Nb and Ti; at least one element selected from the group consisting of Zr, B, and W; or Ca, singly or in combination. Preferably, the steel pipe has a martensitic structure containing 5 to 25 percent by volume of a residual austenite phase, or further containing 5% percent by volume or less of a ferrite phase. Thus, the resulting stainless steel pipe for oil country tubular goods exhibits a superior corrosion resistance even in extremely severe, corrosive environments containing carbon dioxide gas (CO 2 ), chloride ions (Cl − ), or the like.

TECHNICAL FIELD

[0001] The present invention relates to steel pipes for oil country tubular goods used in crude oil wells and natural gas wells. In particular, the present invention relates to an improvement of corrosion resistance to extremely severe, corrosive environment in which carbon dioxide gas (CO₂), chloride ions (Cl⁻), and the like are present.

BACKGROUND ART

[0002] Deep oil wells, which have not conventionally been regarded at all, and corrosive sour gas wells, the development of which was abandoned for a time, have recently been developed increasingly on a world scale in order to cope with increase of crude oil price and anticipated oil resource depletion in the near future. These oil wells and gas wells generally lie at great depths in a severe, corrosive environment of a high-temperature atmosphere containing corrosive substances, such as CO₂ and Cl⁻. Accordingly, steel pipes for oil country tubular goods used for digging such an oil or gas well have to be highly strong and corrosion-resistant.

[0003] In general, highly CO₂ corrosion-resistant 13%-Cr martensitic stainless steel pipes are used in oil wells and gas wells whose atmospheres contain CO₂₁ Cl⁻, or the like. However, conventional martensitic stainless steels cannot wear in environments at high temperatures of more than 100° C. containing a large amount of Cl⁻. Accordingly, two-phase stainless steel pipes are used in oil wells requiring corrosion resistance. Unfortunately, the two-phase stainless steel pipes contain large amounts of alloying elements to reduce the hot workability. Consequently, they must be manufactured only by special heat treatment due to their reduced hot workability, and besides, they are disadvantageously expensive. Accordingly, an inexpensive 13%-Cr martensitic stainless steel-based pipe for oil country tubular goods having a superior hot workability and CO₂ corrosion resistance has been strongly desired. On the other hand, oil well development in cold districts has recently become active, and, accordingly, superior toughness at low temperatures is often required in addition to high strength.

[0004] To these demands, improved martensitic stainless steels (or steel pipes) based on a 13%-Cr martensitic stainless steel (or steel pipe), having an enhanced corrosion resistance have been proposed in, for example, Japanese Unexamined Patent Application Publication Nos. 8-120345, 9-268349, and 10-1755 and Japanese Patent Nos. 2814528 and 3251648.

[0005] Japanese Unexamined Patent Application Publication No. 8-120345 has disclosed a method for manufacturing a seamless martensitic stainless steel pipe having a superior corrosion resistance. For a steel composition of a 13%-Cr martensitic stainless steel pipe, the C content is limited to the range of 0.005% to 0.05%, 2.4% to 6% of Ni and 0.2% to 4% of Cu are added in combination, and 0.5% to 3% of Mo is further added. Furthermore, Ni_(eq) is set at 10.5 or more. This steel material is subjected to hot working, subsequently cooled at air-cooling speed or more, and then tempered. Alternatively, after being cooled, the steel material is further heated to a temperature between A_(C3) transformation point +10° C. and A_(C3) transformation point +200° C., or a temperature between A_(C1) transformation point and A_(C3) transformation point, subsequently cooled to room temperature at air-cooling speed or more, and then tempered. According to this method, a seamless martensitic stainless steel pipe is achieved which has a high strength of the grade API-C95 or grater, corrosion resistance in environments at 180° C. or more containing CO₂, and SCC resistance.

[0006] Japanese Unexamined Patent Application Publication No. 9-268349 has disclosed a method for manufacturing a martensitic stainless steel having a superior stress-corrosion cracking resistance to sulfides. In this method, a steel composition of a 13%-Cr martensitic stainless steel contains 0.005% to 0.05% of C, 0.005% to 0.1% of N, 3.0% to 6.0% of Ni, 0.5% to 3% of Cu, and 0.5% to 3% of Mo. After hot working and being left to cool down to room temperature, this steel material is heated to a temperature between (A_(C1) point+10° C.) and (A_(C1) point+40° C.) for 30 to 60 minutes, then cooled to a temperature of Ms point or less, and tempered at a temperature of A_(C1) point or less. Thus, the resulting steel has a structure in which tempered martensite and 20 percent by volume or more of γ phase are mixed. According to this method, the sulfide stress-corrosion cracking resistance is remarkably enhanced by forming a martensitic structure containing 20 percent by volume or more of γ phase.

[0007] Japanese Unexamined Patent Application Publication No. 10-1755 has disclosed a martensitic stainless steel containing 10% to 15% of Cr, having a superior corrosion resistance and sulfide stress-corrosion cracking resistance. This martensitic stainless steel has a composition in which the Cr content is set at 10% to 15%; the C content is limited to the range of 0.005% to 0.05%; 4.0% or more of Ni and 0.5% to 3% of Cu are added in combination; and 1.0% to 3.0% of Mo is further added. Furthermore, Ni_(eq) of the composition is set at −10 or more. The structure of the martensitic stainless steel contains a tempered martensitic phase, a martensitic phase, and a residual austenitic phase. The total percentage of the tempered martensitic phase and the martensitic phase is set in the range of 60% to 90%. According to this disclosure, corrosion resistance and sulfide stress-corrosion cracking resistance in environments where wet carbon dioxide gas or wet hydrogen sulfide is present are enhanced.

[0008] Japanese Patent No. 2814528 relates to an oil well martensitic stainless steel product having a superior sulfide stress-corrosion cracking resistance. This steel product has a steel composition containing more than 15% and 19% or less of Cr, 0.05% or less of C, 0.1% or less of N, 3.5% to 8.0% of Ni, and 0.1% to 4.0% of Mo, and simultaneously satisfying the relationships: 30Cr+36Mo+14Si−28Ni≦455 (%); and 21Cr+25Mo+17Si+35Ni≦731 (%). According to this disclosure, the resulting steel product exhibits a superior corrosion resistance in severe environments in oil wells where chloride ions, carbon dioxide gas, and a small amount of hydrogen sulfide gas are present.

[0009] Japanese Patent No. 3251648 relates to a precipitation hardening martensitic stainless steel having superior strength and toughness. This martensitic stainless steel has a steel composition containing 10.0% to 17% of Cr, 0.08% or less of C, 0.015% or less of N, 6.0% to 10.0% of Ni, 0.5% to 2.0% of Cu, and 0.5% to 3.0% of Mo. The structure of the steel is formed by 35% or more cold working and annealing and it has a mean crystal grain size of 25 μm or less and precipitates with a particle size of 5×10⁻² μm or more in the matrix. The number of the precipitates is limited to 6×10⁶ per square millimeter or less. According to this disclosure, a high-strength precipitation hardening martensitic stainless steel in which toughness degradation does not occur can be achieved by forming a structure containing fine crystal grains and less precipitation.

DISCLOSURE OF INVENTION

[0010] However, improved 13%-Cr martensitic stainless steel pipes manufactured by the techniques of Japanese Unexamined Patent Application Publication Nos. 8-120345, 9-268349, and 10-1755 and Japanese Patent Nos. 2814528 and 3251648 do not stably exhibit desired corrosion resistance in severe, corrosive environments at temperatures of more than 180° C. containing CO₂, Cl⁻, or the like.

[0011] In view of the circumstances of the known arts stated above, the present invention has been achieved. The object of the present invention is to provide an inexpensive, corrosion-resistant stainless steel pipe for oil country tubular goods, preferably a high-strength stainless steel pipe for oil country tubular goods, having a superior hot workability and exhibiting a superior CO₂ corrosion resistance even in severe, corrosive environments at temperatures of more than 180° C. containing CO₂, Cl⁻, or the like.

[0012] The present invention is as follows:

[0013] (1) A corrosion-resistant stainless steel pipe for oil country tubular goods having a steel composition comprising, on a mass basis, 0.05% or less of C; 0.50% or less of Si; 0.20% to 1.80% of Mn; 0.03 or less of P; 0.005% or less of S; 14.0% to 18.0% of Cr; 5.0% to 8.0% of Ni; 1.5% to 3.5% of Mo; 0.5% to 3.5% of Cu; 0.05% or less of Al; 0.20% or less of V; 0.01% to 0.15% of N; 0.006% or less of O and the balance being Fe and incidental impurities. The composition satisfies expressions (1) and (2):

Cr+0.65Ni+0.6Mo+0.55Cu+20C≧18.5  (1)

Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2)

[0014] ,where Cr, Ni, Mo, Cu, C, Si, Mn, and N represent their respective contents on a mass % basis.

[0015] (2) A corrosion-resistant stainless steel pipe for oil country tubular goods according to (1) in which the composition further contains at least one element of 0.20% or less of Nb and 0.30% or less of Ti on a mass basis.

[0016] (3) A corrosion-resistant stainless steel pipe for oil country tubular goods according to (1) or (2) in which the composition further contains at least one element selected from the group consisting of 0.20% or less of Zr, 0.01% or less of B, and 3.0% or less of W on a mass basis.

[0017] (4) A corrosion-resistant stainless steel pipe for oil country tubular goods according to any one of (1) to (3) in which the composition further contains 0.0005% to 0.01% of Ca on a mass basis.

[0018] (5) A stainless steel pipe for oil country tubular goods according to any one of (1) to (4) and whose structure includes 5 to 25 percent by volume of a residual austenitic phase and the balance being a martensitic phase.

[0019] (6) A corrosion-resistant stainless steel pipe for oil country tubular goods according to any one of (1) to (4) and whose structure includes 5 to 25 percent by volume of a residual austenitic phase, 5 percent by volume or less of a ferrite phase, and the balance being a martensitic phase.

[0020] (7) A method for manufacturing a corrosion-resistant stainless steel pipe for oil country tubular goods including the steps of: forming a steel pipe from a steel pipe material having a composition; quenching the steel pipe by heating the steel pipe to a temperature of the A_(C3) transformation point thereof or more and subsequently cooling to room temperature at air-cooling speed or more; and then tempering the steel pipe at a temperature of the A_(C1) transformation point thereof or less. The composition contains, on a mass basis, 0.05% or less of C; 0.50% or less of Si; 0.20% to 1.80% of Mn; 0.03 or less of P; 0.005% or less of S; 14.0% to 18.0% of Cr; 5.0% to 8.0% of Ni; 1.5% to 3.5% of Mo; 0.5% to 3.5% of Cu; 0.05% or less of Al; 0.20% or less of V; 0.01% to 0.15% of N; 0.006% or less of 0, and the balance being Fe and incidental impurities, and the composition satisfies expressions (1) and (2):

Cr+0.65Ni+0.6Mo+0.55Cu+20C≧18.5  (1)

Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2)

[0021] where Cr, Ni, Mo, Cu, C, Si, Mn, and N represent their respective contents.

[0022] (8) A method for manufacturing a stainless steel pipe for oil country tubular goods according to (7) in which the composition further contains at least one element of 0.20% or less of Nb and 0.30% or less of Ti on a mass basis.

[0023] (9) A method for manufacturing a stainless steel pipe for oil country tubular goods according to (8) in which the quenching includes heating to a temperature in the range of 800 to 1100° C. and cooling to room temperature at air-cooling speed or more, and the tempering is performed at a temperature in the range of 500 to 630° C.

[0024] (10) A method for manufacturing a stainless steel pipe for oil country tubular goods according to any one of (7) to (9) in which the composition further contains at least one element selected from the group consisting of 0.20% or less of Zr, 0.01% or less of B, and 3.0% or less of W on a mass basis.

[0025] (11) A method for manufacturing a stainless steel pipe for oil country tubular goods according to any one of (7) to (10) in which the composition further contains 0.0005% to 0.01% of Ca on a mass basis.

[0026] (12) A method for manufacturing a corrosion-resistant seamless stainless steel pipe for oil country tubular goods, including the steps of: forming a steel pipe from a steel pipe material having a composition by hot working; cooling the steel pipe to room temperature at air-cooling speed or more, or quenching the steel pipe by further heating to a temperature of the A_(C3) transformation point thereof or more and cooling to room temperature at air-cooking speed or more; and then tempering the steel pipe at a temperature of the A_(C1) transformation point thereof or less. The composition contains, on a mass basis, 0.05% or less of C; 0.50% or less of Si; 0.20% to 1.80% of Mn; 0.03 or less of P; 0.005% or less of S; 14.0% to 18.0% of Cr; 5.0% to 8.0% of Ni; 1.5% to 3.5% of Mo; 0.5% to 3.5% of Cu; 0.05% or less of Al; 0.20% or less of V; 0.01% to 0.15% of N; 0.006% or less of O, and the balance being Fe and incidental impurities, and the composition satisfies expressions (1) and (2):

Cr+0.65Ni+0.6Mo+0.55Cu+20C>18.5  (1)

Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2)

[0027] ,where Cr, Ni, Mo, Cu, C, Si, Mn, and N represent their respective contents on a mass % basis.

[0028] (13) A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to (12) in which the composition further contains at least one element of 0.20% or less of Nb and 0.30% or less of Ti on a mass basis.

[0029] (14) A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to (13) in which the quenching includes heating to a temperature in the range of 800 to 1100° C. and cooling to room temperature at air-cooling speed or more, and the tempering is performed at a temperature in the range of 500 to 630° C.

[0030] (15) A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to any one of (12) to (14) in which the composition further contains at least one element selected from the group consisting of 0.20% or less of Zr, 0.01% or less of B, and 3.0% or less of W on a mass basis.

[0031] (16) A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to any one of (12) to (15) in which the composition further contains 0.0005% to 0.01% of Ca on a mass basis.

BEST MODE FOR CARRYING OUT THE INVENTION

[0032] “High strength” in the present invention refers to a strength (yield strength: 550 MPa or more) that conventional 13%-Cr martensitic stainless steel pipes for oil country tubular goods have, and preferably to a yield strength of 654 MPa or more.

[0033] In order to accomplish the above-described objects, the inventors of the present invention have conducted intensive research on the effects of alloying element contents to corrosion resistance in corrosive environments at high temperatures in the range of more than 180° C. to 230° C. containing CO₂₁ Cl⁻, or the like, based on the compositions of the improved 13%-Cr martensitic stainless steel pipes.

[0034] As a result, it has been found that both of a favorable hot workability and a superior corrosion resistance in severe, corrosive environments can be ensured by reducing the C content to be lower than that of the known 13%-Cr martensitic stainless steels and adding suitable amounts of Ni, Mo, and Cu to adjust alloying element contents, so as to satisfy following expressions (1) and (2):

Cr+0.65Ni+0.6Mo+0.55Cu−20C≧18.5  (1)

Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2)

[0035] wherein Cr, Ni, Mo, Cu, C, Si, Mn, and N represent their respective contents (mass %). Furthermore, it has been found that a high strength of 654 MPa or more in terms of yield strength can be ensured.

[0036] The present invention has been completed based on these findings.

[0037] The reason why the steel compositions are controlled will now be explained. Hereinafter, mass percent is expressed by simply %.

[0038] C: 0.05% or Less

[0039] C is an essential element relating to the strength of martensitic stainless steel, but a C content of more than 0.05% promotes sensitization at the stage of tempering due to the presence of Ni. In order to prevent the sensitization at the stage of tempering, the C content is limited to 0.05% or less, in the present invention. In view of corrosion resistance, it is preferable that the C content be set as lower as possible. Preferably, it is 0.03% or less. More preferably, it is set in the range of 0.01% to 0.03%.

[0040] Si: 0.50% or Less

[0041] The element Si serves as a deoxidizer, and, preferably, its content is 0.05% or more in the present invention. However, a content of more than 0.50% reduces the CO₂ corrosion resistance and further reduces the hot workability. Accordingly, the Si content is limited to 0.50% or less. Preferably, it is set in the range of 0.10% to 0.30%.

[0042] Mn: 0.20% to 1.80%

[0043] The element Mn enhances steel strength. In order to ensure a strength desired in the present invention, the Mn content has to be 0.20% or more. However, a content of more than 1.80% negatively affects the toughness. Accordingly, the Mn content is limited to the range of 0.20% to 1.80%. Preferably, it is set in the range of 0.20% to 1.00%. More preferably, it is set in the range of 0.20% to 0.80%.

[0044] P: 0.03% or Less

[0045] The element P negatively affects the CO₂ corrosion resistance, CO₂ stress-corrosion cracking resistance, pitting corrosion resistance, and sulfide stress-corrosion cracking resistance, and it is preferable that the P content be reduced as low as possible. However, an excessive reduction of P content increases cost. Accordingly, the P content is limited to 0.03% or less so as to allow industrial production at a low cost and prevent the degradation of CO₂ corrosion resistance, CO₂ stress-corrosion cracking resistance, pitting corrosion resistance, and sulfide stress-corrosion resistance. Preferably, it is set at 0.02% or less.

[0046] S: 0.005% or Less

[0047] The element S seriously reduces hot workability in manufacture of pipes, and the S content is, preferably, as low as possible. A S content of 0.005% or less makes it possible to manufacture pipes through a common process, and, therefore, the S content is limited to 0.005% or less. Preferably, it is set at 0.003% or less.

[0048] Cr: 14.0% to 18.0%

[0049] The element Cr forms a protective film on the surface of steel to increase the corrosion resistance, and particularly to increase the CO₂ corrosion resistance and CO₂ stress-corrosion cracking resistance. In the present invention, a Cr content of 14.0% or more is necessary from the viewpoint of increasing the corrosion resistance at high temperatures. However, a content of more than 18.0% reduces the hot workability. Accordingly, the Cr content is limited to the range of 14.0% to 18.0%, in the present invention. Preferably, it is set in the range of 14.5% to 17.5%.

[0050] Ni: 5.0% to 8.0%

[0051] The element Ni strengthens the protective film on the surface of steel to enhance the CO₂ corrosion resistance and CO₂ stress-corrosion cracking resistance, pitting corrosion resistance, and sulfide stress-corrosion cracking resistance. Furthermore, it has the effect of a solid solution strengthening and, accordingly, increases steel strength. These effects are exhibited when the Ni content is 5.0% or more. However, a content of more than 8.0% reduces the stability of the martensitic structure to decrease the strength. Accordingly, the Ni content is limited to the range of 5.0% to 8.0%. Preferably, it is set in the range of 5.5% to 7.0%.

[0052] Mo: 1.5% to 3.5%

[0053] The element Mo enhances the resistance to pitting by Cl⁻, and a content of 1.5% or more is necessary in the present invention. While a content of less than 1.5% does not efficiently achieve the corrosion resistance in severe, corrosive environments at high temperatures, a content of more than 3.5% causes the formation of 6-ferrite to reduce the hot workability, CO₂ corrosion resistance, and CO₂ stress-corrosion cracking resistance and increases cost. Accordingly, the Mo content is limited to the range of 1.5% to 3.5%. Preferably, it is set in the range of 1.5% to 2.5%.

[0054] Cu: 0.5% to 3.5%

[0055] The element Cu strengthens the protective film on the surface of the steel to prevent from hydrogen-penetration into the steel, thereby enhancing the sulfide stress-corrosion cracking resistance. This effect is achieved when the Cu content is 0.5% or more. However, a content of more than 3.5% allows CuS to precipitate in grain boundaries to reduce the hot workability. Accordingly, the Cu content is limited to the range of 0.5% to 3.5%. Preferably, it is set in the range of 0.5% to 2.5%.

[0056] Al: 0.05% or Less

[0057] The element Al has a strong effect of deoxidation, but a content of more than 0.05% negatively affects the toughness of the steel. Accordingly, the Al content is limited to 0.05% or less. Preferably, it is set in the range of 0.01% to 0.03%.

[0058] V: 0.20% or Less

[0059] The element V enhances the strength of steel and also has the effect of improving the stress-corrosion cracking resistance. These effects are noticeably exhibited when the V content is 0.03% or more. However, a content of more than 0.20% reduces the toughness. Accordingly, the V content is limited to 0.20% or less. Preferably, it is set in the range of 0.03% to 0.08%.

[0060] N: 0.01% to 0.15%

[0061] The element N extremely enhances the pitting corrosion resistance. This effect is exhibited when the N content is 0.01% or more. However, a content of more than 0.15% allows the formation of various nitrides to reduce the toughness. Accordingly, the N content is limited to the range of 0.01% to 0.15%. Preferably, it is set in the range of 0.03% to 0.15%, and more preferably in the range of 0.03% to 0.08%.

[0062] O: 0.006% or Less

[0063] The element O is present in oxide forms in steel and negatively affects various characteristics. It is, therefore, preferable to be reduced as low as possible. In particular, an O content of more than 0.006% seriously reduces the hot workability, CO₂ stress-corrosion cracking resistance, pitting corrosion resistance, sulfide stress-corrosion cracking resistance, and toughness. Accordingly, the O content is limited to 0.006% or less.

[0064] In the present invention, the above-described basic composition may further contain at least either 0.20% or less of Nb or 0.30% or less of Ti.

[0065] Both the elements Nb and Ti enhance the strength and the toughness, and particularly increase the strength remarkably by tempering at a relatively low temperature in the range of 500 to 630° C. This effect is noticeably exhibited when the Nb and Ti contents are 0.02% or more and 0.01% or more, respectively. On the other hand, a Nb content of more than 0.20% and a Ti content of more than 0.30% reduce the toughness. In addition, Ti has the effect of improving the stress-corrosion cracking resistance. Accordingly, the Nb content is preferably limited to 0.20% or less, and the Ti content, 0.30% or less.

[0066] In the present invention, the above-described composition may further contain at least one element selected from the group consisting of 0.20% or less of Zr, 0.01% or less of B, and 3.0% or less of W.

[0067] Zr, B, and W each increases the strength, and at least one of them may be added if necessary. In addition to the effect of increasing the strength, Zr, B, and W can improve the stress-corrosion cracking resistance. These effects are noticeably exhibited when the composition contains 0.01% or more of Zr, 0.0005% or more of B, or 0.1% or more of W. On the other hand, if the composition contains more than 0.20% of Zr, more than 0.01% of B, or more than 3.0% of W, the toughness is reduced. Accordingly, the Zr content is preferably limited to 0.20% or less; the B content, 0.01% or less; and the W content, 3.0% or less.

[0068] In the present invention, the composition may further contain 0.0005% to 0.01% of Ca.

[0069] The element Ca forms CaS to fix the element S and, thus, to spheroidize sulfide inclusions, thereby reducing lattice distortion of the matrix in the vicinity of the inclusions to reduce the capability of trapping hydrogen of the inclusions advantageously. This effect is achieved when the Ca content is 0.0005% or more. However, a content of more than 0.01% increases CaO, and reduces the CO₂ corrosion resistance and pitting resistance. Accordingly, the Ca content is preferably limited to the range of 0.0005% to 0.01%.

[0070] In addition to the above-described requirements, the each element content have to satisfy following expressions (1) and (2):

Cr+0.65Ni+0.6Mo+0.55Cu−20C≧18.5  (1)

Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2)

[0071] wherein Cr, Ni, Mo, Cu, C, Si, Mn, and N represent their respective contents.

[0072] By adjusting the Cr, Ni, Mo, Cu, and C contents so as to satisfy expression (1), the corrosion resistance in environments at high temperatures up to 230° C. including CO₂ or Cl⁻is remarkably increased. Also, by adjusting the Cr, Mo, Si, C, Mn, Ni, Cu, and N contents so as to satisfy expression (2), the hot workability is enhanced. In the present invention, P, S, and O contents are significantly reduced in order to enhance the hot workability. However, reducing the P, S, and O contents is not enough to ensure a hot workability sufficient to produce seamless martensitic stainless steel pipes. In order to ensure a hot workability sufficient to make seamless martensitic stainless steel pipes, it is important to extremely reduce the P, S, and O contents, and besides to adjust the Cr, Mo, Si, C, Mn, Ni, Cu, and N contents so as to satisfy expression (2).

[0073] The balance of the foregoing elements is Fe and incidental impurities.

[0074] Preferably, the steel pipe of the present invention has a structure comprising 5% to 25% of residual austenite phase on a volume basis and the balance being a martensite phase. Alternatively, the steel pipe of the present invention has a structure comprising 5% to 25% of residual austenite phase, 5% or less of ferrite phase, and the balance being a martensite phase on a volume basis.

[0075] Although the structure of the steel pipe of the present invention is essentially composed of the martensite phase, the martensite phase, preferably, contains 5% to 25% of a residual austenite phase, or further contains 5% or less of a ferrite phase, on a volume basis.

[0076] By allowing 5 percent by volume or more of residual austenite phase to be present, a high toughness can be achieved. However, more than 25 percent by volume of residual austenite phase reduces the strength. Accordingly, it is preferable that the percentage of the residual austenite phase is set in the range of 5 to 25 percent by volume. In addition, in order to enhance the corrosion resistance, it is preferable that 5 percent by volume or less of ferrite phase is allowed to be present. However, more than 5 percent by volume of ferrite phase remarkably reduces the hot workability. Accordingly, it is preferable that the percentage of the ferrite phase is set at 5 percent by volume or less.

[0077] A method for manufacturing the steel pipe of the present invention will now be described taking a seamless steel pipe as an example.

[0078] First, it is preferable that a molten steel having the above-described composition be melted by a conventional steel making process using a converter, an electric furnace, a vacuum melting furnace, or the like, and then formed into a steel pipe material, such as, a billet by a conventional method, such as continuous casting or ingot making-slabbing. Then, the steel pipe material is heated and subjected to hot working to make a pipe by a common manufacturing process, such as that of Mannesmann-plug mill or Mannesmann-mandrel mill. Thus a seamless steel pipe with a desired size is yielded. After pipe making, the resulting seamless steel pipe is preferably cooled to room temperature at air-cooling speed or more.

[0079] The seamless steel pipe having the above-described steel composition can be given a structure mainly composed of a martensite phase by cooling at air-cooling speed or more after hot working. After the cooling at air-cooling speed or more, preferably, quenching is performed in which the steel pipe is heated again to a temperature of the A_(C3) transformation point or more and cooled to room temperature at air-cooling speed or more. Thus, the martensitic structure can be refined and the toughness of the steel can be increased.

[0080] Preferably, the quenched seamless steel pipe is subjected to tempering by being heated to a temperature of the A_(C1) transformation point or less. By heating to a temperature of the A_(C1) transformation point or less, preferably to 400° C. or more, for tempering, the resultant structure comprises a tempered martensite phase, further comprises a residual austenite phase, or still further comprises a small amount of ferrite phase in some cases. Thus, the resulting seamless steel pipe exhibits a desired strength, a desired toughness, and a desired, superior corrosion resistance.

[0081] Only tempering may be performed without quenching.

[0082] The description above illustrates a steel pipe of the present invention taking the seamless steel pipe as an example, but the present invention is not limited to this form. A steel pipe material having the composition within the scope of the present invention may result in an electric welded steel pipe or a UOE steel pipe used as a steel pipe for oil country tubular goods through a conventional process. However, for the electric welded steel tube and UOE steel pipe, it is preferable that, after pipe making, the pipe is quenched by heating the pipe again to a temperature of the A_(C3) transformation point or more and cooling to room temperature at air-cooling speed or more, and is subsequently tempered at a temperature of the A_(C1) transformation point or less.

[0083] In the case of a steel pipe having a composition containing at least one element of Nb and Ti, quenching includes heating to a temperature of 800 to 1100° C., and cooling to room temperature at air-cooling speed or more. Also, tempering is preferably performed at a temperature in the range of 500 to 630° C. By subjecting the steel pipe having the composition containing at least one element of Nb and Ti to these quenching and tempering, a sufficient amount of fine precipitates can occur to achieve a high strength of 654 MPa or more in terms of yield strength.

[0084] A quenching temperature of less than 800° C. does not sufficiently achieve the effect of tempering to provide a desired strength. On the other hand, a quenching temperature of more than 1100° C. coarsens the crystal grains to reduce the toughness of the steel. While a tempering temperature of less than 500° C. does not pricipitate a sufficient amount of precipitations, a tempering temperature of more than 630° C. remarkably reduces the strength of the steel.

EXAMPLES

[0085] The present invention will be further described in detail with reference to Examples.

Example 1

[0086] After degassing, each molten steel having a composition shown in Table 1 was cast into a steel ingot of 100 kgf (980 N). The ingot was subjected to hot working to make a pipe with a model seamless rolling mill, followed by air cooling to yield a seamless steel pipe with an outer diameter of 3.3 in. by a thickness of 0.5 in.

[0087] The hot workability was evaluated by visually observing the presence of cracks in the internal and external surfaces of the resulting seamless steel pipe as air-cooled after pipe making.

[0088] The seamless steel pipe was cut into a test piece. The test piece was heated at 920° C. for 1 hour and then water-cooled. The test piece was further subjected to tempering at 600° C. for 30 minutes. It was ensured that quenching was performed on each sample at a temperature of its A_(C3) transformation point or more, and that tempering was performed at a temperature of its A_(C1) transformation point or less. The quench-tempered test piece was machined into a corrosion-test piece of 3 mm in thickness by 30 mm in width by 40 mm in length, followed by a corrosion test. Some of the steel pipe samples were subjected to only tempering without quenching.

[0089] In the corrosion test, the test piece was immersed in a test solution being 20% NaCl aqueous solution placed in an autoclave (solution temperature: 230° C., CO₂ gas atmosphere at a pressure of 100 atmospheres) and was allowed to keep for 2 weeks.

[0090] The test piece after the corrosion test was weighed, and the corrosion rate was obtained from the difference between the weight of the test piece before the test and that after the test. The surface of the corrosion test piece after the test was observed to check for the occurrence of pitting with a loupe of a magnification of 10 times.

[0091] The results are shown in Table 2. TABLE 1 Ex- Ex- pres- pres- Chemical composition (mass %) sion sion Steel No. C Si Mn P S Al Cr Ni Mo Cu V N O Other (1)* (2)** Remarks A 0.019 0.19 0.48 0.02 0.001 0.01 14.8 5.19 1.60 0.65 0.049 0.059 0.0019 19.11 9.5225 Example B 0.024 0.20 0.44 0.02 0.001 0.01 14.9 5.50 1.50 0.59 0.051 0.062 0.0025 Nb: 0.026 19.22 9.005  Example C 0.015 0.24 0.46 0.03 0.001 0.02 15.3 6.12 2.04 1.05 0.059 0.043 0.0037 Zr: 0.017 20.78 9.7535 Example D 0.025 0.22 0.50 0.01 0.002 0.01 15.1 5.59 2.49 1.63 0.048 0.072 0.0021 Ti: 0.034 20.62 9.6415 Example E 0.027 0.20 0.42 0.01 0.001 0.02 15.5 6.27 1.75 0.77 0.040 0.033 0.0018 20.51 9.1695 Example F 0.024 0.21 0.40 0.02 0.001 0.01 16.2 5.93 1.66 1.14 0.041 0.039 0.0019 Ti: 0.021, 21.20 10.096  Example B: 0.001 G 0.020 2.26 0.41 0.01 0.001 0.01 16.5 6.05 2.17 0.88 0.030 0.054 0.0026 Ca: 0.002 21.82 10.914  Example H 0.016 0.33 0.40 0.01 0.001 0.02 16.9 5.99 1.52 1.02 0.052 0.095 0.0036 Nb: 0.019, 21.95 10.512  Example Ca: 0.001 I 0.026 0.28 0.48 0.01 0.001 0.01 17.3 6.54 1.69 0.64 0.049 0.066 0.0030 W: 0.270 22.40 10.425  Example J 0.017 0.27 0.49 0.01 0.001 0.01 17.7 7.05 1.53 0.85 0.042 0.069 0.0016 B: 0.001 23.33  10.4495 Example K 0.034 0.27 0.50 0.02 0.001 0.02 17.4 5.58 2.87 0.67 0.046 0.056 0.0028 22.44 12.387 Com- parative Example L 0.022 0.26 0.45 0.02 0.001 0.01 13.8 6.19 1.68 0.71 0.055 0.106 0.0017 18.78 7.064  Com- parative Example M 0.045 0.31 0.49 0.01 0.002 0.01 14.6 5.11 1.55 0.59 0.048 0.042 0.0024 Ti: 0.024 18.28 8.4245 Comp- parative Example N 0.020 0.26 0.42 0.03 0.002 0.02 14.7 4.55 1.53 0.69 0.063 0.059 0.0026 18.56 9.982  Com- parative Example O 0.016 0.33 0.44 0.01 0.001 0.01 14.8 5.27 0.56 0.73 0.065 0.058 0.0034 18.64 8.576  Com- parative Example P 0.021 0.21 0.44 0.02 0.001 0.02 17.1 5.15 1.96 0.57 0.056 0.062 0.0028 Nb: 0.033 21.52 12.1545  Com- parative Example Q 0.026 0.35 0.39 0.02 0.001 0.02 14.6 5.19 1.64 0.26 0.045 0.038 0.0019 — 19.10 9.45  Com- parative Example

[0092] TABLE 2 Corrosion Cooling resistance Steel after Quenching Tempering Hot Corrosion pipe Steel pipe- Temp Temp workability rate No. No. making (° C.) Cooling (° C.) Cooling Crack (mm/yr) Pitting Remarks 1 A Air 920 Air 600 Air Good 0.113 Good Example 2 B Air 920 Air 600 Air Good 0.102 Good Example 3 C Air 920 Air 600 Air Good 0.091 Good Example 4 D Air 920 Air 600 Air Good 0.092 Good Example 5 E Air 920 Air 600 Air Good 0.091 Good Example 6 F Air 920 Air 600 Air Good 0.063 Good Example 7 G Air 920 Air 600 Air Good 0.061 Good Example 8 H Air 920 Air 600 Air Good 0.045 Good Example 9 I Air 920 Air 600 Air Good 0.036 Good Example 10 J Air 920 Air 600 Air Good 0.044 Good Example 11 K Air 920 Air 600 Air Good 0.036 Good Comparative Example 12 L Air 920 Air 600 Air Good 0.149 Good Comparative Example 13 M Air 920 Air 600 Air Good 0.162 Good Comparative Example 14 N Air 920 Air 600 Air Good 0.132 Good Comparative Example 15 O Air 920 Air 600 Air Bad 0.179 Bad Comparative Example 16 P Air 920 Air 600 Air Good 0.078 Good Comparative Example 17 Q Air 920 Air 600 Air Good 0.119 Bad Comparative Example 18 A Air — — 600 Air Good 0.107 Good Example

[0093] Each example of the present invention exhibited no occurrence of cracks in the steel pipe surfaces, a low corrosion rate, and no occurrence of pitting. Hence, it has been shown that the steel pipes of these examples have a superior hot workability and a superior corrosion resistance in a severe, corrosive environment at a high temperature of 230° C. containing CO₂. In contrast, comparative examples outside the scope of the present invention exhibited occurrence of cracks, thus showing a reduced hot workability, or exhibited a high corrosion rate, thus showing a reduced corrosion resistance. In particular, there were surface flaws in the steel pipes of comparative examples not satisfying expression (2) due to a reduced hot workability.

Example 2

[0094] After sufficient degassing, each molten steel having a composition shown in Table 3 was cast into a steel ingot of 100 kgf (980 N). The ingot was formed into a seamless steel pipe with an outer diameter of 3.3 in. by a thickness of 0.5 in. with a model seamless rolling mill.

[0095] After the pipe making, the hot workability was evaluated by visually observing the presence of cracks in the internal and external surfaces of the resulting seamless steel pipe.

[0096] The seamless steel pipe was cut into a test piece. The test piece was subjected to quenching and tempering under the conditions shown in Table 4. An ark-shaped API tensile test piece was taken from the quench-tempered test piece and subjected to a tensile test for the tensile properties (yield strength YS, tensile strength TS). Also, a corrosion-test piece of 3 mm in thickness by 30 mm in width by 40 mm in length was taken from the foregoing quench-tempered test piece by machining, and was subjected to a corrosion test.

[0097] In the corrosion test, the test piece was immersed in a test solution being 20% NaCl aqueous solution placed in an autoclave (solution temperature: 230° C., CO₂ gas atmosphere at a pressure of 30 atmospheres) and was allowed to keep for 2 weeks.

[0098] The test piece after the corrosion test was weighed, and the corrosion rate was obtained from the difference between the weight of the corrosion test piece before the test and that after the test. The surface of the corrosion test piece after the test was observed to check for the occurrence of pitting with a loupe of a magnification of 10 times. The results are shown in Table 4. TABLE 3 Ex- Ex- pres- pres- Steel Chemical composition (mass %) sion sion Re- No. C Si Mn P S Al Cr Ni Mo Cu V N O Nb Ti Other (1)* (2)** marks 2A 0.025 0.19 0.34 0.02 0.001 0.01 14.7 6.20 1.90 0.65 0.044 0.059 0.0019 0.074 — — 19.84  8.45 Ex- ample 2B 0.022 0.29 0.49 0.02 0.001 0.01 14.9 5.85 1.94 0.65 0.049 0.078 0.0015 — 0.077 — 19.78  9.03 Ex- ample 2C 0.034 0.18 0.56 0.02 0.001 0.02 14.9 6.13 2.06 0.71 0.035 0.045 0.0021 0.049 0.072 — 19.83  8.56 Ex- ample 2D 0.028 0.31 0.41 0.01 0.002 0.01 15.1 7.03 1.63 0.58 0.059 0.052 0.0027 0.087 — Zr: 20.41  7.77 Ex- 0.061 ample 2E 0.015 0.17 0.36 0.02 0.001 0.02 15.4 6.17 2.34 1.24 0.064 0.042 0.0047 0.038 0.075 B: 21.20 10.07 Ex- 0.001 ample 2F 0.027 0.30 0.35 0.02 0.001 0.01 16.8 7.06 1.71 0.62 0.080 0.320 0.0026 0.089 0.036 Ca: 22.22  7.16 Ex- 0.003 ample 2G 0.017 0.25 0.44 0.01 0.001 0.01 16.7 6.29 1.77 0.91 0.040 0.062 0.0017 0.087 0.042 W: 22.01 10.51 Ex- 0.220 ample 2H 0.028 0.24 0.39 0.01 0.001 0.02 17.2 6.34 1.59 0.74 0.037 0.099 0.0028 — 0.150 Zr: 22.12 10.04 Ex- 0.083 ample Ca: 0.001 2I 0.035 0.35 0.39 0.02 0.001 0.01 17.1 5.96 2.81 0.63 0.049 0.029 0.0051 0.078 — — 22.31 11.93 Com- parative Ex- ample 2J 0.046 0.30 0.40 0.02 0.001 0.01 13.4 5.30 2.57 2.48 0.062 0.053 0.0026 — 0.062 — 18.83  7.38 Com- parative Ex- ample 2K 0.023 0.25 0.36 0.01 0.002 0.01 14.3 5.05 1.55 0.59 0.056 0.059 0.0022 0.073 0.047 Zr: 18.38  9.02 Com- 0.024 parative Ex- ample 2L 0.035 0.26 0.45 0.02 0.002 0.02 15.4 4.06 1.63 0.53 0.051 0.071 0.0019 0.049 0.023 Ca: 18.61 10.55 Com- 0.003 parative Ex- ample

[0099] TABLE 4 Corrosion Cooling Tensile resistance Steel after Quenching Tempering properties Hot Corrosion pipe Steel pipe- Temp Temp YS TS workability rate No. No. making (° C.) Cooling (° C.) Cooling MPa MPa Crack (mm/yr) Pitting Remark 21 2A Air 890 Air 530 Air 910 1138 Good 0.115 Good Example 22 2A Air 890 Air 610 Air 874 1110 Good 0.112 Good Example 23 2B Air 890 Air 530 Air 926 1123 Good 0.109 Good Example 24 2B Air 890 Air 610 Air 891 1049 Good 0.118 Good Example 25 2C Air 890 Air 580 Air 892 1032 Good 0.104 Good Example 2D Air 890 Air 580 Air 821 1004 Good 0.065 Good Example 27 2E Air 890 Air 580 Air 836 966 Good 0.071 Good Example 28 2F Air 890 Air 580 Air 715 884 Good 0.053 Good Example 29 2G Air 890 Air 580 Air 723 901 Good 0.049 Good Example 30 2H Air 890 Air 580 Air 720 877 Good 0.051 Good Example 31 2I Air 890 Air 580 Air 713 864 Bad 0.056 Good Comparative Example 32 2J Air 890 Air 580 Air 908 1073 Good 0.172 Good Comparative Example 33 2K Air 890 Air 580 Air 875 943 Good 0.148 Good Comparative Example 34 2L Air 890 Air 580 Air 892 968 Good 0.162 Good Comparative Example 35 2A Air 780 Air 600 Air 469 934 Good 0.109 Good Example 36 2B Air 760 Air 600 Air 492 972 Good 0.113 Good Example 37 2G Air 890 Air 650 Air 603 783 Good 0.044 Good Example 38 2H Air 910 Air 640 Air 613 768 Good 0.046 Good Example

[0100] Each example of the present invention exhibited no occurrence of cracks in the steel pipe surfaces, a low corrosion rate, and no occurrence of pitting. Hence, it was shown that the steel pipes of these examples had a superior hot workability and a superior corrosion resistance in a severe, corrosive environment at a high temperature of 230° C. containing CO₂. In contrast, comparative examples outside the scope of the present invention exhibited occurrence of cracks, thus showing a reduced hot workability, or exhibited a high corrosion rate, thus showing a reduced corrosion resistance. When the manufacture conditions were outside the preferred ranges as set forth in the present invention, the strength was reduced and, accordingly, a high yield strength of 654 MPa or more was not achieved.

Example 3

[0101] After sufficient degassing, each molten steel having a composition shown in Table 5 was cast into a steel ingot of 100 kgf (980 N). The ingot was formed into a seamless steel pipe with an outer diameter of 3.3 in. by a thickness of 0.5 in. with a model seamless rolling mill.

[0102] The hot workability was evaluated by visually observing the presence of cracks in the internal and external surfaces of the resulting seamless steel pipe, as in Example 1.

[0103] The seamless steel pipe was cut into a test piece. The test piece was subjected to quenching and tempering under the conditions shown in Table 6. It was ensured that quenching was performed on each sample at a temperature of its A_(C3) transformation point or more, and that tempering was performed at a temperature of its A_(C1) transformation point or less. A structure observation test piece was taken from the quench-tempered test piece. The structure observation test piece was etched by aqua regia. The resulting structure was observed with a scanning electron microscope (1000 times), and the percentage of the ferrite phase (percent by volume) was computed with an image analysis system. The percentage of the residual austenite phase was determined by X-ray diffraction.

[0104] An ark-shaped API tensile test piece was taken from the quench-tempered test piece and subjected to a tensile test for the tensile properties (yield strength YS, tensile strength TS), as in Example 1. Also, a V-notch test piece (thickness: 5 mm) was taken from the quench-tempered test piece, in accordance with JIS Z 2202, and the Charpy impact test was performed on the V-notch test piece to determine the absorption energy vE⁻⁴⁰ (J) at −40° C. in accordance with JIS Z 2242.

[0105] Furthermore, a corrosion-test piece of 3 mm in thickness by 30 mm in width by 40 mm in length was taken from the foregoing quench-tempered test piece by machining, and was subjected to a corrosion test, as in Example 2.

[0106] In the corrosion test, the test piece was immersed in a test solution being 20% NaCl aqueous solution placed in an autoclave (solution temperature: 230° C., CO₂ gas atmosphere at a pressure of 30 atmospheres) and was allowed to keep for 2 weeks.

[0107] The test piece after the corrosion test was weighed, and the corrosion rate was obtained from the difference between the weight of the test piece before the test and that after the test. The surface of the corrosion test piece after the test was observed to check for the occurrence of pitting with a loupe of a magnification of 10 times.

[0108] The results are shown in Table 6. TABLE 5 Ex- Ex- pres- pres- Steel Chemical composition (mass %) sion sion No. C Si Mn P S Al Cr Ni Mo Cu V N O Other (1)* (2)** Remarks 3A 0.027 0.24 0.31 0.02 0.001 0.01 15.2 6.14 1.60 0.82 0.039 0.049 0.0021 — 20.06 8.75 Example 3B 0.024 0.21 0.34 0.02 0.001 0.01 14.9 5.50 1.50 1.22 0.051 0.062 0.0025 Nb: 0.077 19.57 8.86 Example 3C 0.018 0.23 0.36 0.01 0.002 0.01 16.1 6.22 1.62 1.09 0.059 0.043 0.0037 Zr: 0.017, 21.35 9.93 Example Ca: 0.002 3D 0.028 0.20 0.41 0.02 0.001 0.02 15.1 5.59 2.49 1.63 0.048 0.072 0.0021 Ti: 0.034, 20.56 9.54 Example Nb: 0.058 3E 0.017 0.25 0.29 0.02 0.001 0.01 16.8 6.26 1.57 0.85 0.042 0.069 0.0016 B: 0.001, 21.94 10.45  Example W: 0.19 3F 0.024 0.27 0.35 0.02 0.001 0.02 15.5 4.58 2.87 0.67 0.046 0.056 0.0028 — 20.09 11.98  Comparative Example 3G 0.032 0.26 0.33 0.02 0.001 0.01 13.7 6.19 1.97 0.71 0.055 0.106 0.0017 — 18.66 6.87 Comparative Example 3H 0.035 0.31 0.29 0.02 0.002 0.01 14.5 5.11 1.55 0.59 0.048 0.042 0.0024 Ti: 0.024 18.38 8.94 Comparative Example

[0109] TABLE 6 Corrosion Impact resistance Cooling Structure Tensile property Corro- Steel after Quenching Tempering γ α properties Absorbed Hot sion pipe Steel pipe- Temp Temp quantity quantity YS TS energy workability rate No. No. making (° C.) Cooling (° C.) Cooling vol % vol % MPa MPa E⁻⁴⁰ J Crack (mm/yr) Pitting Remark A1  3A Air 890 Air 550 Air 7.1 — 868 1021 80.2 Good 0.109 Good Example A2  3A Air 890 Air 600 Air 10.9 — 792 1047 86.1 Good 0.107 Good Example A3  3B Air 890 Air 500 Air 6.3 0.3 889 1061 83.4 Good 0.111 Good Example A4  3B Air 890 Air 600 Air 11.2 0.7 847 1030 85.7 Good 0.112 Good Example A5  3C Air 890 Air 550 Air 12.5 1.5 820 1035 91.2 Good 0.058 Good Example A6  3D Air 890 Air 550 Air 16.3 1.9 771 974 95.4 Good 0.102 Good Example A7  3E Air 890 Air 550 Air 22.7 3.8 723 982 95.9 Good 0.039 Good Example A8  3D Air 890 Air 650 Air 26.3 1.7 634 915 104.3 Good 0.105 Good Example A9  3E Air 890 Air 650 Air 29.6 4.0 599 907 107.6 Good 0.037 Good Example A10 3F Air 890 Air 500 Air 3.2 5.4 999 1149 42.3 Bad 0.096 Good Comparative Example A11 3G Air 890 Air 550 Air 6.1 — 875 1095 79.3 Good 0.179 Bad Comparative Example A12 3H Air 890 Air 540 Air 7.3 2.7 827 1046 77.0 Good 0.150 Good Comparative Example A13 3A Air 890 Air 450 Air — — 949 1018 37.5 Good 0.124 Good Example

[0110] Each example of the present invention exhibited no occurrence of cracks in the steel pipe surfaces, a low corrosion rate, and no occurrence of pitting; hence it was shown that steel pipes of these examples had a superior hot workability. In addition, their structure containing 5 to 25 percent by volume of residual austenite phase, or further containing 5 percent by volume or less of ferrite phase leads to a superior corrosion resistance in a severe, corrosive environment at a high temperature of 230° C. containing CO₂. Furthermore, the strength is as high as 654 MPa or more in terms of yield strength YS and the toughness is as high as 60 J or more in terms of absorbed energy at −40° C.

[0111] In contrast, comparative examples outside the scope of the present invention exhibited occurrence of cracks, thus showing a reduced hot workability, or exhibited a high corrosion rate, thus showing a reduced corrosion resistance. When the manufacture conditions were outside the preferred ranges as set forth in the present invention, the strength was decreased and, accordingly, a high yield strength of 654 MPa or more was not achieved.

INDUSTRIAL APPLICABILITY

[0112] According to the present invention, a high-strength martensitic stainless steel pipe for oil country tubular goods can be manufactured at a low cost with stability which has a sufficient corrosion resistance in severe, corrosive environments at high temperatures containing CO₂ or Cl⁻ or which has a high toughness in addition to such a sufficient corrosion resistance, thus producing particularly advantageous industrial effects. 

1. A corrosion-resistant stainless steel pipe for oil country tubular goods having a steel composition comprising on a mass basis: 0.05% or less of C; 0.50% or less of Si; 0.20% to 1.80% of Mn; 0.03 or less of P; 0.005% or less of S; 14.0% to 18.0% of Cr; 5.0% to 8.0% of Ni; 1.5% to 3.5% of Mo; 0.5% to 3.5% of Cu; 0.05% or less of Al; 0.20% or less of V; 0.01% to 0.15% of N; 0.006% or less of O, and the balance being Fe and incidental impurities, wherein the composition satisfies expressions (1) and (2): Cr+0.65Ni+0.6Mo+0.55Cu+20C≧18.5  (1); Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2), where Cr, Ni, Mo, Cu, C, Si, Mn, and N represent the respective contents thereof on a mass % basis.
 2. A stainless steel pipe for oil country tubular goods according to claim 1, wherein the composition further comprises at least one element selected from the group consisting of 0.20% or less of Nb and 0.30% or less of Ti on a mass basis.
 3. A stainless steel pipe for oil country tubular goods according to claim 1 or 2, wherein the composition further comprises at least one element selected from the group consisting of 0.20% or less of Zr, 0.01% or less of B, and 3.0% or less of W on a mass basis.
 4. A stainless steel pipe for oil country tubular goods according to claims 1, wherein the composition further comprises 0.0005% to 0.01% of Ca on a mass basis.
 5. A stainless steel pipe for oil country tubular goods according to claims 1, wherein the structure thereof includes 5 to 25 percent by volume of a residual austenite phase and the balance being a martensite phase.
 6. A stainless steel pipe for oil country tubular goods according to claims 1, wherein the structure thereof includes, on a volume basis, 5 to 25 percent by volume of a residual austenite phase, 5 percent by volume or less of a ferrite phase, and the balance being a martensite phase.
 7. (A method for manufacturing a corrosion-resistant stainless steel pipe for oil country tubular goods comprising the steps of: forming a steel pipe from a steel pipe material having a composition; quenching the steel pipe by heating the steel pipe to a temperature of the A_(C3) transformation point thereof or more and subsequently cooling to room temperature at air-cooling speed or more; and then tempering the steel pipe at a temperature of the A_(C1) transformation point thereof or less, wherein the composition comprises on a mass basis: 0.05% or less of C; 0.50% or less of Si; 0.20% to 1.80% of Mn; 0.03 or less of P; 0.005% or less of S; 14.0% to 18.0% of Cr; 5.0% to 8.0% of Ni; 1.5% to 3.5% of Mo; 0.5% to 3.5% of Cu; 0.05% or less of Al; 0.20% or less of V; 0.01% to 0.15% of N; 0.006% or less of O, and the balance being Fe and incidental impurities, wherein the composition satisfies expressions (1) and (2): Cr+0.65Ni+0.6Mo+0.55Cu+20C≧18.5  (1); Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2), where Cr, Ni, Mo, Cu, C, Si, Mn, and N represent the respective contents thereof on a mass % basis.
 8. A method for manufacturing a stainless steel pipe for oil country tubular goods according to claim 7, wherein the composition further comprises at least one element of 0.20% or less of Nb and 0.30% or less of Ti on a mass basis.
 9. A method for manufacturing a stainless steel pipe for oil country tubular goods according to claim 8, wherein the quenching includes heating to a temperature in the range of 800 to 1100° C. and cooling to room temperature at air-cooling speed or more, and the tempering is performed at a temperature in the range of 500 to 630° C.
 10. A method for manufacturing a stainless steel pipe for oil country tubular goods according to any one of claims 7 to 9, wherein the composition further comprises at least one element selected from the group consisting of 0.20% or less of Zr, 0.01% or less of B, and 3.0% or less of W on a mass basis.
 11. A method for manufacturing a stainless steel pipe for oil country tubular goods according to claims 7, wherein the composition further comprises 0.0005% to 0.01% of Ca on a mass basis.
 12. A method for manufacturing a corrosion-resistant seamless stainless steel pipe for oil country tubular goods, comprising the steps of: forming a steel pipe from a steel pipe material having a composition by hot working; cooling the steel pipe to room temperature at air-cooling speed or more, or quenching the steel pipe by further heating to a temperature of the A_(C3) transformation point thereof or more and cooling to room temperature at air cooking speed or more; and then tempering the steel pipe at a temperature of the A_(C1) transformation point thereof or less, wherein the composition comprises on a mass basis: 0.05% or less of C; 0.50% or less of Si; 0.20% to 1.80% of Mn; 0.03 or less of P; 0.005% or less of S; 14.0% to 18.0% of Cr; 5.0% to 8.0% of Ni; 1.5% to 3.5% of Mo; 0.5% to 3.5% of Cu; 0.05% or less of Al; 0.20% or less of V; 0.01% to 0.15% of N; 0.006% or less of O, and the balance being Fe and incidental impurities, and wherein the composition satisfies expressions (1) and (2): Cr+0.65Ni+0.6Mo+0.55Cu+20C≧18.5  (1); Cr+Mo+0.3Si−43.5C−0.4Mn−Ni−0.3Cu−9N≦11  (2), where Cr, Ni, Mo, Cu, C, Si, Mn, and N represent the respective contents thereof on a mass % basis.
 13. A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to claim 12, wherein the composition further comprises at least one element of 0.20% or less of Nb and 0.30% or less of Ti on a mass basis.
 14. A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to claim 13, wherein the quenching includes heating to a temperature in the range of 800 to 1100° C. and cooling to room temperature at air-cooling speed or more, and the tempering is performed at a temperature in the range of 500 to 630° C.
 15. A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to any one of claims 12 to 14, wherein the composition further comprises at least one element selected from the group consisting of 0.20% or less of Zr, 0.01% or less of B, and 3.0% or less of W on a mass basis.
 16. A method for manufacturing a seamless stainless steel pipe for oil country tubular goods according to claims 12, wherein the composition further comprises 0.0005% to 0.01% of Ca on a mass basis. 